Abstract
Biodegradable poly(butylene succinate‐co‐terephthalate)(PBST) copolyester, with 70 mol % butylene terephthalate (BT), was melt‐spun into fibers at various take‐up velocities ranging from 2.0 to 4.0 km/min. The structure development and mechanical properties of the as‐spun PBST fibers were intensively investigated via birefringence, wide angle X‐ray diffraction (WAXD) measurement, tensile test, and cyclic stretch test. With increasing the take‐up velocity, the initial tensile modulus and breaking strength of PBST fibers increased, while elongation at break decreased. These were attributed to the increasing degree of orientation and crystallinity, which were resulted from the elevating tension of spinning line at higher take‐up velocity. To elucidate the effects of soft butylene succinate (BS) unit on the tensile and elastic properties of PBST fibers, poly(butylene terephthalate) (PBT) fibers were adopted as a comparison sample. The results showed that the combination of soft BS unit and hard BT unit for PBST fibers made contribution to the lower initial modulus, higher elongation at break and better elastic recovery than those of PBT fibers. Moreover, PBST fibers were found to undergo PBT‐like crystal form transition from α‐form to β‐form crystal structure under tension load through the measurement of WAXD. A relatively wider strain region for the crystal transition of PBST fibers also endowed them with higher elastic recoverability than PBT fibers. © 2012 Wiley Periodicals, Inc. J Appl Polym Sci, 2012
<!--Unmatched element: w:blockFixed-->| Authors: | Luo, Shengli; Li, Faxue; Yu, Jianyong; Cao, Amin | |
| Journal: | Journal of Applied Polymer Science | |
| Volume: | 125 | |
| Issue: | 3 | |
| Year: | 2012 | |
| Pages: | 2426 | |
| DOI: | 10.1002/app.36506 | |
| Publication date: | 05-08-2012 |
Watchlist
This is where you can add this publication to your personal favourites.
Additional Information
Vesicle‐Mediated Growth of Tubular Branches and Centimeter‐Long Microtubes from a Single Molecule
Abstract The mechanism by which small molecules assemble into microscale tubular structures in aqueous solution remains poorly understood, particularly when the initial building blocks are non‐amphiphilic molecules and no surfactant is used. It is here shown how a subnanometric molecule ... more
The image illustrates a natural phenomenon of droplet formation caused by the condensation of vapor on a nonwettable surface at temperature below the dew point. Real‐time observing the light scattered from the droplets may lead to a new mechanism for vapor sensing. However, the dew point ... more
NO is a key vasodilator in mammalian cardiovascular systems and has been shown to sensitize tissue to γ‐radiation. However, photochemical NO precursors that can be activated by these NIR wavelengths are extremely limited. G. D. Stucky, D. Zhao, P. C. Ford, F. Zhang and co‐workers have ad ... more
Bioengineers Succeed in Producing Plastic Without the use of Fossil Fuels
A team of pioneering South Korean scientists have succeeded in producing the polymers used for everyday plastics through bioengineering, rather than through the use of fossil fuel based chemicals. This groundbreaking research, which may now allow for the production of environmentally consci ... more
In the past, restoration of paintings and other old artwork often involved application of acrylic resins to consolidate and protect them. One of the most important tasks for modern restorers is thus to remove these layers, because it turns out that acrylic resins not only drastically change ... more
Is trash the solution to tackling climate change?
Converting the trash that fills the world's landfills into biofuel may be the answer to both the growing energy crisis and to tackling carbon emissions, claim scientists in Singapore and Switzerland. New research published in Global Change Biology: Bioenergy, reveals how replacing gasoline ... more
Über CHEMIE.DE
CHEMIE.DE Information Service GmbH runs specialist scientific internet portals. The secret to our success? We are familiar with what we publish.
Advertising at CHEMIE.DE
Our advertising formats support you in getting your message across to a clearly defined target audience.
© 1997-2013 CHEMIE.DE Information Service GmbH, All rights reserved
Netmeeting