Red plague (corrosion)



Bold text:For other meanings, see red plague.

Additional recommended knowledge

'Red plague is an accelerated corrosion of copper when plated with silver. After storage or use in high-humidity environment, cuprous oxide forms on the surface of the parts. The corrosion is identifiable by presence of patches of brown-red powder deposit on the exposed copper.

Red plague is caused by normally occurring electrochemical potential between the copper and silver, leading to galvanic corrosion occurring in pits or breaks in the silver plating. It develops in the presence of moisture and oxygen when the porosity of the silver layer allows them to come in contact with the copper-silver interface. It is an electrochemical corrosion - a copper-silver galvanic cell forms and the copper acts as sacrificial anode. In suitable conditions, the corrosion can proceed rather quickly and lead to total circuit failure.

 
This article is licensed under the GNU Free Documentation License. It uses material from the Wikipedia article "Red_plague_(corrosion)". A list of authors is available in Wikipedia.
Your browser is not current. Microsoft Internet Explorer 6.0 does not support some functions on Chemie.DE