Neodymium-doped yttrium orthovanadate

Neodymium-doped yttrium orthovanadate (Nd:YVO₄) is a crystalline material formed by adding neodymium ions to yttrium orthovanadate. It is commonly used as an active laser medium for diode-pumped solid-state lasers. It comes as a transparent blue-tinted material. It is birefringent, therefore rods made of it are usually rectangular.

Product highlight

Revolutionize your production: real-time Raman analysis for maximum efficiency

Ion chromatography - automated for high sample volumes

Potentiostat/galvanostat of the latest generation

Basic properties

• Atomic density: ~1.37×10²⁰ atoms/cm²

• Crystal structure:
  • zircon tetragonal (tetragonal bipyramidal)
  • space group D_4h
  • a=b=7.12, c=6.29

• Density: 4.22 g/cm²

• Mohs hardness: Glass-like, ~5

• Thermal expansion coefficient:
  • α_a=4.43×10^-6/K
  • α_c=11.37×10^-6/K

• Thermal conductivity:
  • parallel to C-axis: 5.23 W·m^-1·K^-1
  • perpendicular to C-axis: 5.10 W·m^-1·K^-1

Optical properties

• Lasing wavelengths : 914 nm, 1064 nm, 1342 nm

• Crystal class : positive uniaxial, n_o=n_a=n_b, n_e=n_c,
  • n_o=1.9573, n_e=2.1652, at 1064 nm
  • n_o=1.9721, n_e=2.1858, at 808 nm
  • n_o=2.0210, n_e=2.2560, at 532 nm

• Fluorescence lifetime (spontaneous emission lifetime) as a function of Nd ions concentration:

• Absorption cross-section at 808nm : 5.5×10^-20 cm²

• Emission cross-section at 1064nm : 38×10^-19 cm² (Reference: JOSA 66, 1405-1414 (1976).)

• Polarized laser emission : π-polarization; parallel to optic axis (c-axis) (for a-cut crystal)

• Gain bandwidth : 0.96 nm (257 GHz) at 1064 nm (for 1.1 atm% Nd doped)

See also

• Yttrium aluminium garnet (YAG)

References

• . E. Rast, H. H. Caspers, and S. A. Miller (1968). "Infrared Spectral Emittance and Optical Properties of Yttrium Vanadate". Phys. Rev. 169 (3): 705 - 709. doi:10.1103/PhysRev.169.705.
• O. Guillot-Noel, B. Bellamy, B. Viana, D. Gourier (1999). "Correlation between rare-earth oscillator strengths and rare-earth–valence-band interactions in neodymium-doped YMO4 (M=V, P, As), Y3Al5O12, and LiYF4 matrices". Phys. Rev. B 60 (3): 1668 - 1677. doi:10.1103/PhysRevB.60.1668.